Since the white fiber is produced by the film splitting method, the dispersion in fineness is relatively large, generally from 2dtex to 10dtex. The brown fiber is wet-spinned, so the fiber fineness is relatively fixed. At present, it is 3.3dtex in foreign countries, and the single yarn strength is generally above 4dtex in China. The length is generally 51mm~75mm. The melting point of PTFE is 327 °C, and it can be used for a long time at a high temperature of 260 °C, and the instantaneous use temperature can exceed 300 °C. PTFE cannot burn, and its limiting oxygen index reaches 95%. The strength is low and the breaking elongation is small. The breaking strength of the imported brown fiber is only 1.9cn/dtex, while the strength of the white imported fiber basically does not exceed 4cn/dtex. The friction coefficient is low, so the dust is easy to fall off on the surface of the filter material. The surface tension of the fiber is large, and it has good water repellency. The fiber is finer, the filtration efficiency is average, and the filter material has a weight of 750-800g. The textile performance is not good, the cohesive force is low, and static electricity is easily generated in the fiber spinning process.

The chemical name of PPS is polyphenylene sulfide. It is a white material with excellent thermal stability. Although it will burn when it is placed in a flame, the combustion will stop immediately when the flame is removed. It will show a yellow-orange flame when it burns, and a trace of black will be generated. Soot does not fall off the burned material, and forms residual coke, showing low flame spread and smoke density. The limiting oxygen index is 34-35. The most commonly used fineness is: 2.2 dtex. Other finenesses are: 1.1 dtex 1.7 dtex 3.0 dtex and so on. The most commonly used lengths: 51mm and 60mm. The working temperature is 130～160℃, the short-term working temperature is 190℃, and the melting point is 285℃. In addition, the oxygen content of the fiber should be less than 8% during normal use. The higher the oxygen content, the use temperature should decrease accordingly.

Bag filters are in general frequently used for dust removal in industrial applications. Filter bags come in a wide range of fabrics, coatings, finishes, sizes and configurations.

Dust filtration-----filter bag and filter felt Polyester filter bag,polyester antistatic filter bag,polyester blending filter bag,polyester filter bag with membrane,polyester filter bag water and oil repellent,polyester filter bag special type,aramid filter bag pps filter bag, acrylic filter bag, p84 filter bag, ptfe filter bag,fms filter bag,fiberglass filter bag,PTFE mix pps filter bag and polyester needle punched felt,acylic felt,aramid felt,P84 felt so on.

Dust collection bags play an important role in the development of modern industry and are widely used in the environmental protection of atmospheric dust in the food, chemical, biomass power generation, and pharmaceutical industries. PTFE dust bag has excellent performance under certain harsh operating conditions, such as strong temperature resistance, abrasion resistance, corrosion resistance, chemical resistance, high filtration efficiency, low running resistance, long service life, etc. Advantages, so it is widely used in various harsh flue gas filtering environments such as steel, electricity, garbage incineration, etc.

In the industrial flue gas dust removal, due to the different characteristics of the steel, cement, power generation, waste incineration and other industries and the differences in the operating conditions of the enterprises themselves, it is more difficult to grasp the operating conditions of the manufacturers. Therefore, in addition to the quality of the filter material itself, in terms of the external environment, there are many factors that affect the service life of the dust bag, but the main factors are the amount of flue gas, the amount of dust in the flue gas, soot particles, and the types of flue gas substances.

The chemical name of PPS is polyphenylene sulfide. It is a white material with excellent thermal stability. Although it will burn when it is placed in a flame, the combustion will stop immediately when the flame is removed. It will show a yellow-orange flame when it burns, and a trace of black will be generated. Soot does not fall off the burned material, and forms residual coke, showing low flame spread and smoke density. The limiting oxygen index is 34-35. The most commonly used fineness is: 2.2 dtex. Other finenesses are: 1.1 dtex 1.7 dtex 3.0 dtex and so on. The most commonly used lengths: 51mm and 60mm. The working temperature is 130～160℃, the short-term working temperature is 190℃, and the melting point is 285℃. In addition, the oxygen content of the fiber should be less than 8% during normal use. The higher the oxygen content, the use temperature should decrease accordingly.

Bag filters are in general frequently used for dust removal in industrial applications. We make filter bags to fit most styles and types of bag houses and other dust collection systems. Filter bags come in a wide range of fabrics, coatings, finishes, sizes and configurations.Medias are available in various fabric weights and treatments such as singed, glazed, PTFE membrane, acid and alkali resistance and Oxidation resistance.

Since the white fiber is produced by the film splitting method, the dispersion in fineness is relatively large, generally from 2dtex to 10dtex. The brown fiber is wet-spinned, so the fiber fineness is relatively fixed. At present, it is 3.3dtex in foreign countries, and the single yarn strength is generally above 4dtex in China. The length is generally 51mm~75mm. The melting point of PTFE is 327 °C, and it can be used for a long time at a high temperature of 260 °C, and the instantaneous use temperature can exceed 300 °C. PTFE cannot burn, and its limiting oxygen index reaches 95%. The strength is low and the breaking elongation is small. The breaking strength of the imported brown fiber is only 1.9cn/dtex, while the strength of the white imported fiber basically does not exceed 4cn/dtex. The friction coefficient is low, so the dust is easy to fall off on the surface of the filter material. The surface tension of the fiber is large, and it has good water repellency. The fiber is finer, the filtration efficiency is average, and the filter material has a weight of 750-800g. The textile performance is not good, the cohesive force is low, and static electricity is easily generated in the fiber spinning process.